Deposition of amorphous aluminium powder using cold spray

Deposition of amorphous aluminium powder using cold spray technology as a corrosion prevention measure was studied. Amorphous aluminium (Al-Ni-Ce) powder was successfully deposited on 7000-series aluminium substrates using cold spray parameters of 1.7 MPa under compressed air and temperature of 450oC. The coatings were subjected to tensile bond strength measurement and comparative studies with cold sprayed pure Al6061 coatings were conducted. The results obtained showed that the amorphous aluminium coatings exhibited better adhesive strength. In addition, salt-water immersion test was conducted. The Al-Ni-Ce coating not only demonstrated better corrosion resistance but also exhibited evidence of passivation of surface imperfections such as scratches in the coatings.