Indentation study on the pressure sensitivity of a ZR-based bulk metallic glass

Spherical indentation test was conducted on as-cast and annealed Zr 41.2Ti13.8Cu12.5Ni10Be 22.5 bulk metallic glass, and the evolution of the morphology of the deformation zone of indents upon annealing was investigated. The DSC traces of the as-cast and annealed samples show that the enthalpy change at the glass transition, ΔH, decreases with the increasing of annealing temperature, indicating the reduction of the free volume upon annealing. The morphology of the indents implies a reduced shear band activity in the annealed samples. The included angles (2θ) between two families of shear bands emanating from the edge of spherical indent in the as-cast and the annealed samples were measured to be in the range of 88-79°, which decrease with the increasing of annealing temperature, indicating pressure sensitive plasticity in the as-cast and annealed samples. By Mohr-Coulomb criterion, the pressure sensitive index, α, can be obtained on the basis of the measured 2θ. The sensitivity index increases with increasing temperature, implying an increase of 'atomistic friction' due to the reduction of the free volume upon annealing.